NiTi形状记忆薄膜的显微结构和力学性能

NiTi形状记忆合金薄膜具有形状记忆效应，极有希望用于制造高技术领域微电子机械系统中的微型激发器。NiTi形状记忆合金薄膜在制备和使用过程中需要高品质（衬）底材。本文利用高分辨电子显微学和高分辨分析电子显微学详细研究了硅底材NiTi形状记忆合金薄膜的NiTi／Si和NiTi／SiO2微结构体系，包括薄膜精细结构和界面反应。也研究了其显微结构和力学性能的关系。特别给出了NiTi形状记忆合金薄膜产生疲劳过程的微观过程的起因，通过高达十万个使用热循环前后样品显微结构变化的比较，发现纳米尺度上的TiNi3新相的形成导致疲劳过程的发生。如何抑制TiNi3新相形成的研究正在进行之中，这将为进一步提高NiTi形状记忆合金的使用寿命指出方向。     

微晶合金在电流互感器中的应用

从微晶合金的性能特点出发，分析了其在电流互感器中的应用前景。     

TiAl基合金板材制备技术的发展现状

综述了TiAl基合金板材制备技术的发展现状。介绍了的制备TiAl基合金板材三种技术的工艺过程及制得的TiAl基合金板材的显微组织和力学性能。     

45钢表面超音速电弧喷涂Ti-Al涂层的组织与性能研究

采用自行开发研制的超音速电弧喷设备，在45钢表面制成了钛铝合金复合涂层。并利用金相显微镜、X射线衍射仪、扫描电镜、电子探针，对涂层的成分、相结构、显微组织及其结合强度、显微硬度进行了研究。结果表明，利用超音速电弧喷涂设备，可以在45钢表面形成 度高、孔隙率低，结合强度较好和硬度高的Ti-Al合金涂层。     

高温预析出对Al-Zn-Mg系铝合金时效硬化和应力腐蚀的影响

研究了高温固溶后降温处理工艺对中强可使预析出LC52和7039铝合金的组织、时效硬化和应力腐蚀的影响。金相观察发现,高温预析出可优先在晶界处产生,并提高随后时效状态下晶界析出相的不连续分布程度,温度降低到一定程度晶内和晶界产生大量析出。合金拉伸性能和应力腐蚀结果表明,预析出在保持强度和塑性的同时,可提高抗应力腐蚀性能。而预析出温度降低,合金强度呈下降趋势。     

Influence of inhibitor addition on the corrosion protection performance of sol–gel coatings on AA2024

Sol–gel films are actively investigated during the last decade as possible candidates for environmentally friendly pre-treatments. However, the important drawback in this case is the lack of active corrosion protection and self-healing ability.     

EIS evaluation of the filiform corrosion of aluminium coated by a cataphoretic paint

Filiform corrosion is mainly considered as a cosmetic attack and is undesirable in most applications. The initiation and propagation of the filaments are related to different parameters such as the presence of defects, the permeability of the coating to water and oxygen, the adherence of the paint system and the presence of salts.

The aim of this work is to study the behaviour of painted aluminium samples towards filiform corrosion or delamination. The 6082 Aluminium alloy was selected and the samples were covered with a cataphoretic epoxy primer without lead (PPG Industries France). Prior to the application of the electrocoat, the samples were pre-treated by a commercial Zr/Ti or chromate conversion treatment or simply etched with a commercial acid etching product.

Filiform corrosion was studied by the normalized test (ISO/DIS 4623): painted and scratched samples were inoculated in HCl and exposed in a constant humidity chamber at 40 °C and 82% RH for 3 weeks. After exposure the samples were subjected to a visual and optical microscopic examination.

Electrochemical impedance spectroscopy was used to study the sensitivity to filiform corrosion. The operating mode of this test is similar to the normalized one. The samples were scratched before inoculation for 1 h in HCl and then exposed to the humidity chamber for a maximum of 4 days. The samples were tested by EIS in an acidified 0.1 M Na₂SO₄ electrolyte solution. The resulting impedance spectra were analyzed with an appropriate equivalent electrical circuit which allows the evaluation of the exposed metallic surface area, directly related to the extent of filiform corrosion or delamination. Different parameters were varied: the exposure time in the humidity chamber; the immersion time in the electrolyte sulphate solution as well as its pH and the coating thickness.     

薄板坯连铸连轧流程Ti微合金化高强钢开发与应用

在薄板坯连铸连轧流程上，经过对Ti微合金化技术研究，有效解决了Ti微合金化强度性能波动大的问题，开发出屈服强度450～700MPa高强钢。对试制钢组织性能和工业应用分析研究，表明该产品通板性能良好，通板强度差30MPa左右；成形性能良好，d=0时冷弯测试全部合格；同时还具有良好焊接性能，焊接后，强度波动较小，均在母材部位断开；试制钢显微组织为珠光体和铁素体，晶粒均匀细小，平均尺寸为4～8／μm；实物质量满足集装箱和汽车制造行业要求，具有广阔市场前景。     

FeBP非晶态合金超细微粒的合成及其对PH3分解的催化作用

用化学还原法合成了FeBP非晶态合金超细微粒，用电感耦合等离子体光谱（ICP）、X射线粉末衍射（XRD）、透射电子显微镜（TEM）和差热分析（DSC）等手段对其进行了物性表征，并用微型催化反应装置考察了其对PH3分解的催化作用，结果表明，非晶态合金FeBP对PH3的分解具有良好的催化作用，能使PH3的分解温度从800℃以上降到500℃左右。490℃时分解率超过90％，540℃时达100％。     